Resin infiltrant for non-cavitated caries lesions: evaluation of color stability
2017
Background The objective of this in vitro study was to evaluate the over time color stability of one resin infiltrant (Icon) upon exposure to staining solutions (coffee and wine) compared with one nano-hybrid sealant (Grandio Seal), one transparent fissure sealant with fluoride (Control Seal) and one nanofilled composite (Filtek Supreme XTE). Material and Methods All materials were polymerized according to manufacturers’ instructions into silicon rings (height 1 mm; internal diameter 6 mm; external diameter 8 mm) to obtain specimens identical in size. The specimens were immersed in staining solutions at room temperature over a 28-day test period. The control samples have not been subjected …
Evaluation of quality changes of blueberry juice during refrigerated storage after high-pressure and pulsed electric fields processing
2012
Abstract A better knowledge of the effect of refrigerated storage on the nutritional and physicochemical characteristics of foods processed by emerging technologies with regard to unprocessed juices is necessary. Thus, blueberry juice was processed by high pressure (HP) (600 MPa/42 °C/5 min) and pulsed electric fields (PEF) (36 kV/cm, 100 μs). The stability of physicochemical parameters, antioxidant compounds (ascorbic acid, total phenolics, total anthocyanins) and antioxidant capacity was studied just after treatment and during 56 days at refrigerated storage at 4 °C. Just after treatment, all treated blueberry juices showed a decrease lower than 5% in ascorbic acid content compared with t…
Color degradation mapping of rock art paintings using microfading spectrometry
2021
[EN] Rock art documentation is a complex task that should be carried out in a complete, rigorous and exhaustive way, in order to take particular actions that allow stakeholders to preserve the archaeological sites under constant deterioration. The pigments used in prehistoric paintings present high light sensitivity and rigorous scientific color degradation mapping is not usually undertaken in overall archaeological sites. Microfading spectrometry is a suitable technique for determining the light-stability of pigments found in rock art paintings in a non-destructive way. Spectral data can be transformed into colorimetric information following the recommendations published by the Commission …
Freshness assessment of gilthead sea bream (Sparus aurata) by machine vision based on gill and eye color changes
2013
Abstract The fish freshness was evaluated using machine vision technique through color changes of eyes and gills of farmed and wild gilthead sea bream ( Sparus aurata ), being employed lightness ( L * ), redness ( a * ), yellowness ( b * ), chroma ( c * ), and total color difference (Δ E ) parameters during fish ice storage. A digital color imaging system, calibrated to provide accurate CIELAB color measurements, was employed to record the visual characteristics of eyes and gills. The region of interest was automatically selected using a computer program developed in MATLAB software. L * , b * , and Δ E of eyes increased with storage time, while c * decreased. The a * parameter of fish eyes…
Effect of 15% carbamide peroxide bleaching gel on color stability of giomer and microfilled composite resin: an in vitro comparison
2011
Objectives: The effect of 15% carbamide peroxide bleaching gel on color stability and surface topography of a giomer and a microfilled composite resin was evaluated in the present in vitro study. Study design: Forty discs measuring 10 mm in diameter and 1 mm in thickness were prepared from a giomer and a microfilled composite resin. Each material yielded 20 discs with completely smooth surfaces. Then a spectrophotometer was used to measure L* (lightness), a* (redness, greenness) and b* (blueness, yellowness) color coordinates of all the discs. Subsequently, the specimens were subjected to 15% carbamide peroxide bleaching gel. After measuring the color coordinates once again, color changes (…
Effect of finishing and polishing systems on the surface roughness and color change of composite resins
2020
Background This study is to examine the surface roughness and color changes occurring on composite resins following the application of different finishing and polishing systems. Material and Methods In our study, a total of 200 samples were prepared from composites resin (6×2 mm) containing supra-nano, submicron hybrid, nanohybrid, nano-ceramic and microhybrid filler. They were polished with diamond, aluminum oxide, silicon carbide finishing and polishing systems. The initial color values of composite samples were measured with a spectrophotometer and surface roughness values with a profilometer. After that, samples were immersed of coffee solution and color measurements were repeated on th…
Effect of two whitening agents on the color of composite dental restorations
2018
Background To evaluate color changes to composite resins used to restore extracted teeth compared with composite discs after whitening with two agents: hydrogen peroxide (HP) and carbamide peroxide (CP). Material and methods Ten human molars with class V vestibular and palatine cavity preparation obturated with Vita hybrid nanocomposite were hemisected to obtain 20 specimens assigned randomly to two groups: O1 and O2. Twenty composite discs were divided into two groups: D1 and D2. The groups O1 and D1 were treated with 16% CP, while groups =2 and D2 were treated with 37.5 % HP. Chromaticity coordinates L*, a* and b* were registered using a spectrophotometer. Results Statistically significan…
Effect of over-the-counter whitening strips and toothpaste on shear bond strength of orthodontic brackets
2021
Background To investigate: 1) the effects of over-the-counter white strip enamel bleaching and 2-Step whitening toothpaste application on the shear bond strength of orthodontic brackets at 24-hours and 7-days post-bleaching latent period; and 2) the correlation between amount of bleaching and shear bond strength. Material and Methods Sixty human premolar teeth were randomly assigned into two bleaching groups, white strip group treated with Crest® 3D WHITE™ LUXE Professional Effects Whitestrips (Proctor & Gamble, Greensboro, NC), and whitening toothpaste group, treated with Crest® 3D WHITE™ BRILLIANCE 2-Step Toothpaste (Proctor & Gamble, Greensboro, NC). The groups were further divided into …
Physicochemical and nutritional characteristics of blueberry juice after high pressure processing
2013
Abstract This study was carried out to investigate the impact of high pressure processing (HPP) at different pressure (200, 400 and 600 MPa) and treatment times (5, 9 and 15 min) on ascorbic acid, total phenolics, anthocyanin stability and total antioxidant capacity, were also studied at different physicochemical parameters such as pH, °Brix and color. HPP treatments resulted in more than 92% vitamin C retention at all treatment intensities. On the other hand, total phenolic content in the juice was increased, mainly after HPP at 200 MPa for all treatment times. The total and monomeric anthocyanin were similar or higher than the value estimated for the fresh juice being maximum at 400 MPa/1…